White aluminum oxide for Billiard Pool Cue Chalk
White Aluminum Oxide (White Fused Alumina) is the premium core raw material engineered for manufacturing high-performance Billiard Pool Cue Chalk. Specially processed for the billiards industry, our white aluminum oxide delivers consistent texture, optimal adhesion, and stable physical properties, making it the top choice for professional cue chalk production.
Crafted from high-purity alumina refined at ultra-high temperatures, this abrasive raw material features uniform particle size distribution, moderate hardness, and excellent fluidity. The fine, even grains ensure the cue chalk holds a compact, crack-resistant cube shape without crumbling or dusting excessively during use. Its smooth particle structure allows the chalk to adhere firmly to the cue tip, enhancing friction between the tip and the cue ball for precise, stable shots—critical for both casual players and professional athletes.
PHYSICAL PROPERTIES-White aluminum oxide for Billiard Pool Cue Chalk
| Specific Weight | 3.96 g/ cm3 |
| Mohs Hardness | 9.0 |
| Crystal form | α-Al2O3 |
| Melting Point | 2250℃ |
TYPICAL CHEMICAL ANALISIS [%]-White aluminum oxide for Billiard Pool Cue Chalk
| Al2O3 | Fe2O3 | SiO2 | FeO | MgO | CaO | TiO2 | Na2O | K2O | LOI |
| 99.2-99.6 | 0.03-0.10 | ≤0.02 | / | ≤0.01 | ≤0.01 | / | 0.20-0.30 | ≤0.02 | < 0.09 |
Our White Aluminum Oxide for billiard chalk is low in impurities, iron-free, and chemically stable, preventing discoloration or residue buildup on cue tips. It supports consistent mixing with binders and pigments, enabling the production of vibrant, long-lasting cue chalk in various colors. The material’s moderate grinding property ensures the chalk glides smoothly onto the tip without scratching or damaging it, extending the service life of cue tips.
Available sizes of White aluminum oxide for Billiard Pool Cue Chalk
| Size | D3(um) | D50(um) | D94（um) |
| F230 | ＜82 | 53.0±3.0 | >34 |
| F240 | ＜70 | 44.5±2.0 | >28 |
| F280 | ＜59 | 36.5±1.5 | >22 |
| F320 | ＜49 | 29.2±1.5 | >16.5 |
| F360 | ＜40 | 22.8±1.5 | >12 |
| F400 | ＜32 | 17.3±1.0 | >8 |
| F500 | ＜25 | 12.8±1.0 | >5 |
| F600 | ＜19 | 9.3±1.0 | >3 |
| F800 | ＜14 | 6.5±1.0 | >2 |
| F1000 | ＜10 | 4.5±0.8 | >1 |
| F1200 | ＜7 | 3.0±0.5 | >1(at 80%) |
| F1500 | ＜5 | 2.0±0.4 | >0.8(at 80%) |
| F2000 | ＜3.5 | 1.2±0.3 | >0.5(at 80%) |
Suitable for all types of billiard cue chalk, including pool, snooker, and carom chalk, this raw material meets strict industrial production standards. It offers excellent batch stability, reliable fluidity for automated molding, and high forming efficiency, greatly improving the quality and consistency of finished cue chalk products.
With high purity, stable particle size, and superior processing performance, our White Aluminum Oxide is the ideal raw material to create professional-grade billiard cue chalk that enhances shot control, reduces miscues, and elevates the overall playing experience. It is the trusted selection for leading cue chalk manufacturers worldwide.