F120 F180 white aluminium oxide for producing ceramic wheels and polishing pasts
F120 and F180 white aluminium oxide powder are high‑purity fused alumina abrasives specially graded for manufacturing ceramic grinding wheels and polishing pastes. Produced by melting high‑grade bauxite under ultra‑high temperature, followed by crushing, magnetic separation, washing and precise particle classification, this white alumina features high hardness, sharp cutting edges, stable chemical properties and good thermal resistance, making it an ideal raw material for advanced abrasive tools and polishing materials.
PHYSICAL PROPERTIES
| Specific Weight | 3.96 g/ cm3 |
| Mohs Hardness | 9.0 |
| Crystal form | α-Al2O3 |
| Melting Point | 2250℃ |
TYPICAL CHEMICAL ANALISIS [%]
| Al2O3 | Fe2O3 | FeO | MgO | CaO | TiO2 | Na2O | K2O | LOI |
| 99.5 | 0.04 | / | 0.01 | 0.01 | / | 0.25 | 0.01 | < 0.09 |
PARTICLE SIZE DISTRIBUTION
| F8 | +4000um | 0 | +2800um | ≤20% | +2360um | ≥45% | +2360+2000um | ≥70% | -1700um | ≤3% |
| F10 | +3350um | 0 | +2360um | ≤20% | +2000um | ≥45% | +2000+1700um | ≥70% | -1400um | ≤3% |
| F12 | +2800um | 0 | +2000um | ≤20% | +1700um | ≥45% | +1700+1400um | ≥70% | -1180um | ≤3% |
| F14 | +2360um | 0 | +1700um | ≤20% | +1400um | ≥45% | +1400+1180um | ≥70% | -1000um | ≤3% |
| F16 | +2000um | 0 | +1400um | ≤20% | +1180um | ≥45% | +1180+1000um | ≥70% | -850um | ≤3% |
| F20 | +1700um | 0 | +1180um | ≤20% | +1000um | ≥45% | +1000+850um | ≥70% | -710um | ≤3% |
| F22 | +1400um | 0 | +1000um | ≤20% | +850um | ≥45% | +850+710um | ≥70% | -600um | ≤3% |
| F24 | +1180um | 0 | +850um | ≤25% | +710um | ≥45% | +710+600um | ≥65% | -500um | ≤3% |
| F30 | +1000um | 0 | +710um | ≤25% | +600um | ≥45% | +600+500um | ≥65% | -425um | ≤3% |
| F36 | +850um | 0 | +600um | ≤25% | +500um | ≥45% | +500+425um | ≥65% | -355um | ≤3% |
| F46 | +600um | 0 | +425um | ≤30% | +355um | ≥40% | 355+300um | ≥65% | -250um | ≤3% |
| F54 | +500um | 0 | +355um | ≤30% | +300um | ≥40% | +300+250um | ≥65% | -212um | ≤3% |
| F60 | +425um | 0 | +300um | ≤30% | +250um | ≥40% | 250+212um | ≥65% | -180um | ≤3% |
| F70 | +355um | 0 | +250um | ≤25% | +212um | ≥40% | +212+180um | ≥65% | -150um | ≤3% |
| F80 | +300um | 0 | +212um | ≤25% | +180um | ≥40% | +180+150um | ≥65% | -125um | ≤3% |
| F90 | +250um | 0 | +180um | ≤20% | +150um | ≥40% | +150+125um | ≥65% | -106um | ≤3% |
| F100 | +212um | 0 | +150um | ≤20% | +125um | ≥40% | +125+106um | ≥65% | -75um | ≤3% |
| F120 | +180um | 0 | +125um | ≤20% | ≥40% | ≥40% | +106+90um | ≥65% | -63um | ≤3% |
| F150 | +150um | 0 | +106um | ≤15% | +75um | ≥40% | +75+63um | ≥65% | -45um | ≤3% |
| F180 | +125um | 0 | +90um | ≤15% | +75um | * | +75+63um | ≥40% | -53um | * |
| F220 | +106um | 0 | +75um | ≤15% | +63um | * | +63+53um | ≥40% | -45um | * |