High Purity White Aluminum Oxide Abrasive for Ship Hull Cleaning
White Aluminum Oxide Abrasive was made from the high quality alumina by melting above 2000 in the electric arc furnace and cooling. It is white with the main crystal phase α-Al2O3.
The white alumina produced in titling electric arc furnace has the advantage of high bulk density and low porosity and the volume stability and thermal shock resistance can be improved.
TYPICAL CHEMICAL ANALISIS [%]
| Al2O3 | Fe2O3 | FeO | MgO | CaO | TiO2 | Na2O | K2O | LOI |
| 99.5 | 0.04 | / | 0.01 | 0.01 | / | 0.25 | 0.01 | < 0.09 |
PPARTICLE SIZE DISTRIBUTION
| F8 | +4000um | 0 | +2800um | ≤20% | +2360um | ≥45% | +2360+2000um | ≥70% | -1700um | ≤3% |
| F10 | +3350um | 0 | +2360um | ≤20% | +2000um | ≥45% | +2000+1700um | ≥70% | -1400um | ≤3% |
| F12 | +2800um | 0 | +2000um | ≤20% | +1700um | ≥45% | +1700+1400um | ≥70% | -1180um | ≤3% |
| F14 | +2360um | 0 | +1700um | ≤20% | +1400um | ≥45% | +1400+1180um | ≥70% | -1000um | ≤3% |
| F16 | +2000um | 0 | +1400um | ≤20% | +1180um | ≥45% | +1180+1000um | ≥70% | -850um | ≤3% |
| F20 | +1700um | 0 | +1180um | ≤20% | +1000um | ≥45% | +1000+850um | ≥70% | -710um | ≤3% |
| F22 | +1400um | 0 | +1000um | ≤20% | +850um | ≥45% | +850+710um | ≥70% | -600um | ≤3% |
| F24 | +1180um | 0 | +850um | ≤25% | +710um | ≥45% | +710+600um | ≥65% | -500um | ≤3% |
| F30 | +1000um | 0 | +710um | ≤25% | +600um | ≥45% | +600+500um | ≥65% | -425um | ≤3% |
| F36 | +850um | 0 | +600um | ≤25% | +500um | ≥45% | +500+425um | ≥65% | -355um | ≤3% |
| F46 | +600um | 0 | +425um | ≤30% | +355um | ≥40% | 355+300um | ≥65% | -250um | ≤3% |
| F54 | +500um | 0 | +355um | ≤30% | +300um | ≥40% | +300+250um | ≥65% | -212um | ≤3% |
| F60 | +425um | 0 | +300um | ≤30% | +250um | ≥40% | 250+212um | ≥65% | -180um | ≤3% |
| F70 | +355um | 0 | +250um | ≤25% | +212um | ≥40% | +212+180um | ≥65% | -150um | ≤3% |
| F80 | +300um | 0 | +212um | ≤25% | +180um | ≥40% | +180+150um | ≥65% | -125um | ≤3% |
| F90 | +250um | 0 | +180um | ≤20% | +150um | ≥40% | +150+125um | ≥65% | -106um | ≤3% |
| F100 | +212um | 0 | +150um | ≤20% | +125um | ≥40% | +125+106um | ≥65% | -75um | ≤3% |
| F120 | +180um | 0 | +125um | ≤20% | ≥40% | ≥40% | +106+90um | ≥65% | -63um | ≤3% |
| F150 | +150um | 0 | +106um | ≤15% | +75um | ≥40% | +75+63um | ≥65% | -45um | ≤3% |
| F180 | +125um | 0 | +90um | ≤15% | +75um | * | +75+63um | ≥40% | -53um | * |
| F220 | +106um | 0 | +75um | ≤15% | +63um | * | +63+53um | ≥40% | -45um | * |
Mainly Applications
-Bonded Abrasives and Coated abrasives
-Creating a matt finish on glass
-Wet and dry blast media,grinding and polishing etc
-Floor/Wall laminates,Wear-resistant
-Thermal spraying/plasma spraying,Processing very hard component
-Catalyst Carrier
-Ceramic and Tiles,Ceramic filter plate,ceramic membrane etc
-Grinding wheels,Cup wheels,Whetstone,polishing pads etc
-Blast-cleaning,surface finishing,Deburring,Roughening metallic surfaces